Technical Datasheet
DESCRIPTION
Terluran GP-35 is high-flow, general purpose injection molding grade with good ductility, intended for moldings with thin walls and/or adverse
flow length to wall ratio.

FEATURES
Excellent colorability
High flowability
Good impact resistance
Good heat distortion resistance
High quality surface finish and gloss

APPLICATIONS
Injection molding
Thin wall components for telecommunications
Household and sanitary appliances
Toys
Automotive components

Property, Test Condition Standard Unit Values
Rheological Properties
Melt Volume Rate 220 °C/10 kg ISO 1133 cm³/10 min 34
Mechanical Properties
Izod Notched Impact Strength, 23 °C ISO 180/A kJ/m² 22
Izod Notched Impact Strength, -30 °C ISO 180/A kJ/m² 7
Charpy Notched Impact Strength, 23° C ISO 179 kJ/m² 19
Charpy Notched Impact Strength, -30° C ISO 179 kJ/m² 7
Charpy Unnotched, 23° C ISO 179 kJ/m² 125
Charpy Unnotched, -30° C ISO 179 kJ/m² 90
Tensile Stress at Yield, 23° C ISO 527 MPa 44
Tensile Strain at Yield, 23° C ISO 527 % 2.4
Tensile Modulus ISO 527 MPa 2300
Nominal Strain at Break, 23 °C ISO 527 % 12
Flexural Strength ISO 178 MPa 65
Hardness, Ball Indentation ISO 2039-1 MPa 99
Thermal Properties
Vicat Softening Temperature VST/B/50 (50°C/h, 50N) ISO 306 °C 95
Vicat Softening Temperature, VST/A/50 (50°C/h, 10N) ISO 306 °C 102
Terluran GP-35
Acrylonitrile Butadiene Styrene (ABS)
Page 2of 3
Revision Date: 2013.08.21
Contact us:
Phone +65 6933 8372
infopoint.asia@styrolution.com
www.styrolution.com
Property, Test Condition Standard Unit Values
Heat Deflection Temperature A; (annealed, 1.8 MPa) ISO 75 °C 92
Heat Deflection Temperature B; (annealed, 0.45 MPa) ISO 75 °C 95
Coefficient of Linear Thermal Expansion ISO 11359 10^(-6)/°C 80 - 110
Thermal Conductivity DIN 52612-1 W/(m K) 0.17
Electrical Properties
Volume Resistivity IEC 60093 Ohm*m 1E13
Other Properties
Density ISO 1183 kg/m³ 1040
Water Absorption, Saturated at 23°C ISO 62 % 0.95
Moisture Absorption, Equilibrium 23°C/50% RH ISO 62 % 0.24
Yellowness Index DIN 6167 - 15
Processing
Linear Mold Shrinkage ISO 294-4 % 0.4 - 0.7
Melt Temperature Range ISO 294 °C 220 - 260
Mold Temperature Range ISO 294 °C 30 - 60
Injection Velocity ISO 294 mm/s 200
Drying Temperature °C 80
Drying Time h 2 - 4
Typical values for uncolored products
SUPPLY FORM
Terluran® is delivered as spherical pellets. The bulk density of the pellets is from 0.55 to 0.65 g/cm³. Standard Packaging unit: 25 kg PE-bag
on palette, shrunk or wrapped with PE film or delivery in silo trucks. PE bags should not be stored outside. In dry areas with normal
temperature control, Terluran pellets can be stored for relatively long periods of time without any change in mechanical properties. Under poor
storage conditions, Terluran absorbs moisture, but this can be removed by drying.