Tên sản phẩm: | Nhựa PC 1070U, Lotte |
---|---|
Mã sản phẩm | Nhựa PC 1070U |
Nhóm sản phẩm: | Hạt nhựa PC |
Lượt xem | 3831 |
Mua hàng | |
Nhựa PC 1070U
Xuất xứ: Lotte, Hàn Quốc
General Information |
Description |
PC-1070U has higher viscosity, impact strength, tensile & flexural strength, and elastic modulus, which can be used in sheet-extrusion and stringent demand such as and goggles etc. PC-1070U have UV stabilized ingredients to prevent degradation of final PC products from lights. |
Applications |
OUTDOOR APPLICATION, MULTI-WALL, SOLID SHEET |
Typical properties1 |
|||
|
Test Method |
Typical value |
Unit |
Physical |
|
|
|
Melt Flow Index, 300℃, 1.2kg |
ASTM D1238 |
7 |
g/10min |
Specific Gravity |
ASTM D792 |
1.20 |
|
Mold Shrinkage |
ASTM D955 |
0.5~0.7 |
% |
Mechanical |
|
|
|
Tensile Strength, yield, 50mm/min |
ASTM D638 |
630 |
kgf/cm2 |
Tensile Elongation, break, 50mm/min |
ASTM D638 |
>100 |
% |
Flexural Strength, yield, 10mm/min |
ASTM D790 |
920 |
kgf/cm2 |
Flexural Modulus, 10mm/min |
ASTM D790 |
24,000 |
kgf/cm2 |
IZOD Impact Strength, notched, 23 ℃, 1/8” |
ASTM D256 |
85 |
kg∙cm/cm |
notched, 23 ℃, 1/4” |
ASTM D256 |
- |
kg∙cm/cm |
Thermal |
|
|
|
Heat Distortion Temp. 4.6kgf/cm2 |
ASTM D648 |
144 |
℃ |
18.6kgf/cm2 |
ASTM D648 |
133 |
℃ |
Vicat Softening Temp. Rate B/50 |
ASTM D1525 |
153 |
℃ |
Optical |
|
|
|
Light Transmittance |
ASTM D1003 |
89 |
% |
Haze |
ASTM D1003 |
< 0.8 |
% |
Refractive Index |
ASTM D542 |
1.585 |
|
Processing guides1 |
||
Typical value |
Unit |
|
Drying condition |
||
120 |
℃ |
|
4 |
hr |
|
0.02 |
% |
|
Injection molding |
||
290 ~ 310 |
℃ |
|
280 ~ 300 |
℃ |
|
290 ~ 310 |
℃ |
|
280 ~ 300 |
℃ |
|
270 ~ 290 |
℃ |
|
60 ~ 80 |
℃ |
|
60 ~ 90 |
℃ |
|